Method for the production of coated, fine-particle, inorganic solids and use thereof

ABSTRACT

Disclosed is a method for producing coated, fine-particle, inorganic solids, the surface of which is coated with fine inorganic solid particles containing at least two different organic additives. At least one of said additives contains a wetting agent, dispersing agent, or deflocculant. The additives represent a maximum of 15 percent by weight of the coated solids.

The invention relates to a process for the preparation of coated finely divided inorganic solids and to their use.

Inorganic solids (e.g. inorganic pigments or fillers) are incorporated inter alia as functional additives in the form of powders or dispersions into synthetic polymers, surface coatings, paints/inks (e.g. printing inks), fibres, paper (e.g. paper for lamination), adhesives, ceramics (e.g. electroceramics and magnetic ceramics), enamels, adsorbents, ion exchangers, grinding and polishing agents, cooling lubricants and cooling lubricant concentrates, refractory products, hard concrete materials, medical products and cosmetics (e.g. powders, ointments, toothpastes). In order that the inorganic solids are able to develop their desired properties in such fields of application, very good and uniform distribution of the finely divided inorganic solids in the particular system in question is desirable. Such uniform distribution is imperative in the case of incorporation into polymers in particular.

In order to improve the processing properties of the finely divided, inorganic solids, DE 198 39 856 A1 has proposed embedding them into a matrix consisting of an organic carrier material, The pulverulent intermediate formed thereby consists of individual particles having a size of <1 μm. Such a particle in turn contains several individual inorganic solids particles, which are embedded in the organic matrix. Disadvtantages of these additives are the relatively high content of organic carrier material and the relatively expensive process for the preparation of these additives.

In DE 100 05 685 A1, it is proposed to coat finely divided barium sulfate with an organic substance, each individual barium sulfate particle being coated with a layer of organic substance. In this process, the filter cake of barium sulfate can be processed to form a paste, with which the organic substance is mixed. The mixture is then dried. In a variant of the process, the filter cake of barium sulfate is dried and then the organic substance is added. Both processes have the disadvantage that the distribution of the organic substance on the barium sulfate particles is not uniform. In a further is process variant it is proposed to suspend the filter cake of barium sulfate in water again, to add the organic substance and then to dry the mixture. Although this process results in better distribution of the organic substance on the barium sulfate particles, it has the disadvantage that a relatively large amount of water is required for preparing the suspension, which water must subsequently be removed again.

The object of the invention is to overcome the disadvantages of the prior art and provide a process with which finely divided inorganic solids can be modified with an organic substance in such a manner that they can readily be incorporated as additives into various systems (e.g. polymers, surface coatings, paints/inks, paper, ceramics, medical products or cosmetic products). In particular, the organic substance is to be distributed uniformly over the surface of the inorganic solids, and the proportion of organic substance is to be less than 15 wt. %, preferably less than 10 wt. %, of the finished additive (coated inorganic finely divided solids). Furthermore, it is to be possible to carry out the preparation process using a smaller amount of water than in processes known hitherto in which the organic substance is added to a suspension of finely divided inorganic solids in water. If required, it is also to be possible to carry out the modification of the finely divided inorganic solids with the organic substance without using any water at all.

The object is achieved by a process in which the surface of finely divided inorganic solids particles is coated with at least two different organic additives, at least one additive comprising a wetting agent, dispersing agent or deflocculating agent and the proportion of additives being not more than 15 wt. %, preferably not more than 10 wt. %, or 5 wt. %, and particularly preferably not more than 3 wt. %, of the coated solids.

There are preferably used as the finely divided inorganic solids, separately or in the form of a mixture, titanium dioxide, barium sulfate, lithopone, zinc sulfide, zinc oxide, calcium carbonate, calcium sulfate, iron oxide, silicon dioxide, talcum, kaolin, mica, aluminium oxide, aluminium hydroxide, metal titanates, coloured titanates (e.g. chrome nickel titanates), zirconium oxide, macnesiurn oxide, hydrotalcite, chalk, mixed-phase pigments, anticorrosive pigments, inorganic flameproofing pigments, black pigments (e.g. iron oxide black), inorganic special-effect pigments, or metal nitrides, carbides and borides.

Wetting, dispersing or deflocculating agent is here to be understood as meaning a surface-active substance which facilitates the dispersion (=breaking up) of a pulverulent substance in a liquid medium by lowering the surface tension between two oppositely charged components by reversal of the charge of the surface. As a result, the agglomerates that are present are broken down in the dispersion process, so that re-agglomeration (=accumulation) or flocculation (=aggregation) is prevented.

As wetting, dispersing or deflocculating agents (referred to only as dispersing agents hereinbelow) there may be used both ionic and non-ionic dispersing is agents. The following substances car: preferably be employed: alkali metal (especially Na and K) salts or ammonium salts of organic acids (e.g. salts of poly(meth)acrylic acid), alkali metal salts of acrylate or methacrylate copolymers (having a preferred molecular weight of up to 15,000), polyphosphates (inorganic or organic polyphosphates, e.g. poly(meth)acrylate phosphates), generally poly(meth)acrylates, polyethers, anionically modified polyethers, fatty alcohol polyglycol ethers, modified polyurethanes or anionically active aliphatic esters.

The added amount of dispersing agent is dependent on the mean particle size of the inorganic solids. The finer the inorganic solids, the greater the added amount of dispersing agent. The added amount of dispersing agent is preferably from 0.01 to 10 wt. %, particularly preferably from 0.01 to 5 wt. %, or from 0.1 to 3 wt. %, based on the finished coated product.

The second organic additive preferably comprises one or more of the following substances: carboxylic acids, soaps, metal soaps, alcohols (e.g. 1,1,1-trimethylol-propane), pentaerythritol, neopentyl glycol, polyglycols (e.g. polyethylene glycol), polyethylene glycol ethers, organic eaters (e.g. neopentyl glycol dibenzoate), silanes, siloxanes, silicone oils, organic sulfones of the formula RSO₂R, organic ketones (R—(C═O)—R), organic nitrites (RCN), organic sulfoxides (R₂-SO₂), organic amides (R—(C═O)-NR′R or R—(S═O)-ONR′R), fatty acid esters or fatty acid amides.

The added amount of the second organic additive is also dependent on the mean particle size of the inorganic solids. The finer the inorganic solids particles, the greater the added amount of the second organic additive. The added amount of the second organic additive is preferably from 0.01 to 10 wt. %, particularly preferably from 0.01 to 5 wt. %, or from 0.1 to 3 wt. %, based on the finished coated product.

The dispersing agent can be added to the finely divided inorganic solids separately or in admixture with the second organic additive. In the case of separate addition, the sequence of addition is in principle unimportant. For practical reasons, however, it is preferable in the case of separate addition first to add the dispersing agent and then to add the second additive.

The finely divided inorganic solids may be in the form of an aqueous suspension or in the form of a filter cake (paste-like or in dough form). It is advantageous to use a filter cake in the undried state (e.g. from current production) because the inorganic particles are then not completely agglomerated and the outlay in terms of dispersion after addition of the dispersing agent and of the second organic additive is thus minimised. If the finely divided inorganic solids are in powder form, it is expedient to carry out wet grinding of the inorganic solids before preparing a suspension. The suspension or filter cake preferably has a solids content of from 15 to 85 wt. %, particularly preferably from 25 to 80 wt. % and very particularly preferably from 50 to 80 wt. %.

Drying of the suspension provided with the additives can be carried out by means of conventional drying units. Spray driers, grinding driers or vacuum driers are preferably used. If required, the dried product can subsequently be ground, for example by means of a steam-jet mill, air-jet mill or pinned disk mill.

Surprisingly, it has been found that, even with a very high solids content, suspensions or filter cakes are liquefied after addition of the dispersing agent and of the second organic additive to such an extent that optimum distribution of the additives on the particle surface is ensured and the resulting suspension can be pumped without difficulty, which reduces the outlay in terms of the process considerably. Owing to the low water content of such a “liquid” suspension, the outlay in terms of drying is also reduced.

It is also possible to mix finely divided inorganic solids in powder form with the dispersing agent and the second organic additive in a mixer and then grind the mixture, for example in a steam-jet mill, air-jet mill or pinned disk mill.

The coated finely divided inorganic solids preferably have a mean particle size d₅₀ of from 0.001 to 20 μm, particularly preferably from 0.005 to 5 μm, very particularly preferably from 0.01 to 2 μm, or from 0.1 to 1 μm.

An advantage of the process according to the invention is that the coated finely divided inorganic solids that are obtained have excellent flowability and can very readily be transported pneumatically. On account of these properties, they can excellently be metered for addition to polymer melts. If the coated finely divided inorganic solids are in turn to be processed further in the form of a suspension or slurry, they can be processed without a high outlay in terms of dispersion to (also non-aqueous) “liquid” dispersions having a high solids content, for example from 30 to 80 wt. %, preferably from 40 to 75 wt. %. It has additionally been found that such suspensions have high stability to storage or, if solids should settle out, can very readily be re-dispersed. There is therefore no agglomeration of the particles.

If undesirable foam formation should occur during the preparation of such a suspension (dispersion in water or an organic solvent), the foam formation can be suppressed by addition of an antifoam. The added amount of antifoam is dependent on the nature of the inorganic solids and on the nature and amount of the dispersing agent used and oil the second organic additive. The added amount may be up to 3 wt. % but is generally less than 1.5 wt. %, in each case based on the solids content of the suspension.

The coated finely divided inorganic solids prepared by the process according to the invention can be used, for example, in plastics, especially in the preparation of polymers (e.g. thermoplastic or thermosetting polymers), in surface coatings, paints/inks (e.g. printing inks), fibres, paper (e.g. paper for lamination), adhesives, ceramics (e.g. electroceramics and magnetic ceramics), enamels, adsorbents, ion exchangers, grinding and polishing agents, cooling lubricants and cooling lubricant concentrates, refractory products, hard concrete materials, medical products and cosmetics (e.g. powders, ointments, toothpastes).

The coated finely divided inorganic solids prepared by the process according to the invention are distributed in polymers much better than finely divided inorganic solids treated according to the prior art. This manifests itself inter aria in the so-called pressure filter test.

The subject-matter of the invention is explained in greater detail by means of Examples:

PREPARATION FOR EXAMPLES A AND 1 Preparation of a BaSO₄ Paste

In known manner, barium sulfate was precipitated from aqueous solution by reaction of barium ions with sulfate ions. The precipitated BaSo₄ was separated from the mother liquor and washed. The resulting paste-like filter cake consisted of 67 wt. % dry matter and 33 wt. % water. The particle size d₅₀ of the BaSO₄ particles was 0.45 μm.

COMPARISON EXAMPLE A Coating of the BaSO₄ Surface with an Additive According to the Prior Art

200 l of demineralised water were placed in a stirrer vessel, and 120 kg of the prepared BaSO₄ paste (contained 80 kg of BaSO₄) were added, with stirring. 1330 ml of an aqueous 1,1,1-trimethylolpropane solution, which contained 600 g of 1,1,1-trimethylolpropane per litre of solution, were then added in portions in the course of 30 minutes under the action of the shearing forces of a dissolver (2000 rpm). 798 g (0.99 wt. %, based on the finished product) of 1,1,1-trimethylolpropane were thus introduced. The mixture was dispersed for a further 15 minutes. The resulting suspension had a solids content of 325 g/l (26.2 wt. %) and was spray-dried under the following conditions:

Inlet temperature 535° C., outlet temperature 135° C., spraying plate 18,000 rpm, throughput 110 l/h.

The resulting pulverulent BaSO₄ with a single-layer coating had a moisture content of 0.15 wt. % and a mean particle size d₅₀ of 0.54 μm.

The suspension proved to be problematical before drying in terms of its stirring and pumping properties. The reason was the high viscosity of the suspension, as was to be expected with a solids content of 26.2 wt. %.

EXAMPLE 1 Coating of the BaSO₄ Surface with a Dispersing Agent and a Second Organic Additive

28 l of demineralised water were placed in a stirrer vessel, and 149 kg of the prepared BaSO₄ paste (contained 99.8 kg of BaSO₄) were added, with stirring. 400 g of a 40% potassium polyacrylate copolymer solution in water (having a mean molar mass of about 5000) were then added in portions in the course of 30 minutes under the action of the shearing forces of a dissolver (2000 rpm). 160 g (0.16 wt. %, based on the finished product) of potassium polyacrylate copolymer were thus introduced. The mixture was dispersed for a further 15 minutes. 1642 ml of an aqueous 1,1,1-trimethylolpropane solution, which is contained 600 g of 1,1,1-trimethylolpropane per litre of solution, were then added in portions, with stirring. 985 g (0.96 wt. %, based on the finished product) of 1,1,1-trimethylolpropane were thus introduced. Stirring was then carried out for a further 15 minutes. The suspension so obtained had a solids content of 960 g/l (55.9 wt. %) and was spray-dried as described in Comparison Example A.

The coated BaSO₄ powder so prepared had a moisture content of 0.15 wt. % and a mean particle size d₅₀ of 0.48 μm.

Despite the very high solids content of 55.9 wt. %, the suspension had a surprisingly low viscosity before drying and accordingly exhibited very good stirring and pumping properties. The suspension could be dried without difficulty.

COMPARISON EXAMPLE B Processing of the Coated BaSO4 from Comparison Example A in a Polymer Melt

In a twin-screw extruder, 27 kg of BaSO₄ powder from Comparison Example A were incorporated into 23 kg of polyethylene terephthalate (PET from KoSa, type: Polyclear 1101). The temperature of the heating zone was 265° C. The concentration of BaSO₄ in the PET masterbatch so prepared was 54 wt. %.

EXAMPLE 2 Processing of the Coated BaSO₄ from Example 1 in a Polymer Melt

Analogously to Comparison Example B, 27 kg of the BaSO₄ powder from Example 1 prepared by the process according to the invention were incorporated into 23 kg of polyethylene terephthalate (PET from KoSa, type: Polyclear 1101).

EXAMPLE 3 Comparison of the Polymers from Example 2 and Comparison Example B by Means of the PF Value

In order to check the distribution of the BaSO₄ solids particles in the polymer, pressure filter tests were carried out on both the 54% BaSO₄/PET masterbatches. The PF value obtained thereby is used as a measure of the quality of masterbatches. The lower the PF value, the better the quality of the masterbatches in terms of the distribution of the inorganic solids particles in the polymer. The masterbatches from Example 2 and Comparison Example B were melted continuously in an extruder and fed to a 14 μm screening cloth (filter area 6.16 cm²). The temperature was 265° C. in the 1st heating zone, 270° C. in the 2nd heating zone and 280° C. in the 3rd, 4th and 5th heating zones. The throughput was about 40 g/minute.

Measurement is complete when a pressure of 200 bar is reached or after 60 minutes at the latest. The pressure filter test values (PF value) are calculated by the following formula: ${PF} = {\frac{\left( {p_{\max} - p_{0}} \right) \times F \times 100}{\left( {t \times K \times G} \right)}\left\lbrack {{bar} \times {cm}^{2}\text{/}g} \right\rbrack}$ wherein:

-   p_(max) =final pressure (bar) -   p₀ =starting pressure (bar) -   F =filter area (cm²) -   t =measuring time (min) -   K =concentration (% pigment) -   G =throughput (g/min)

In this manner, a PF value of 0.87 bar·cm²/g was found for the masterbatch prepared in Comparison Example B and a PF value of only 0.19 bar·cm²/g was found for the masterbatch prepared in the Example according to the invention. This low PF value clearly shows the superiority of the coated finely divided inorganic solids prepared by the process according to the invention when incorporated into polymers. 

1-17. (canceled)
 18. A process comprising coating a surface of finely divided inorganic solid particles at least two different organic additives, wherein at least one additive is a wetting agent, dispersing agent or deflocculating agent, and wherein the proportion of the additives is not more than 15 wt. % of the coated solids, wherein the finely divided inorganic solids are in the form of an aqueous suspension or in the form of a filter cake and the two different organic additives are coated on to the finely divided inorganic solids separately or in the form of a mixture, the resulting suspension being dried and the coated finely divided inorganic solids having a mean particle size d₅₀ of from 0.001 to 20 μm.
 19. A process according to claim 18, wherein the finely divided inorganic solids are in the form of a powder instead of in the form of a suspension or filter cake and are mixed with the two different organic additives in a mixer and the mixture is then ground.
 20. A process according to claim 18, wherein the proportion of additives is not more than 10 wt. % of the coated solids.
 21. A process according to claim 18, wherein the proportion of additives is not more than 5 wt. % of the coated solids.
 22. A process according to claim 18, wherein the finely divided inorganic solids are titanium dioxide, bariun sulfate, lithopone, zinc sulfide, zinc oxide, calcium carbonate, calcium sulfate, iron oxide, silicon dioxide, talcum, kaolin, mica, aluminium oxide, aluminium hydroxide, metal titanates, a colored titanate, zirconium oxide, magnesium oxide, hydrotalcite, chalk, a mixed phase pigment, an anticorrosive pigment, an inorganic flameproofmg pigment, a black pigment, an inorganic special-effect pigment, a metal nitride, a metal or a metal boride.
 23. A process according to claim 18, wherein the wetting, dispersing or deflocculating agent comprises at least one of the substance selected from the group consisting of an alkali metal salt of an organic acid, an ammonium salt of an organic acid, an alkali metal salt of an acrylate copolymer, an alkali metal salt of a methacrylate copolymer, a polyphosphate, a poly (meth)acrylate, a polyether, an anionically modified polyether, a fatty alcohol polyglycol ether, a modified polyurethanes and an anionically active aliphatic ester.
 24. The process according to claim 18, wherein the added amount of wetting, dispersing or deflocculating agent is from 0.001 to 10 wt. %, based on the finished coated product.
 25. The process according to claim 24, wherein the added amount of wetting, dispersing or deflocculating agent is from 0.001 to 5 wt. %, based on the finished coated product.
 26. The process according to claim 18, wherein the second organic additive comprises at least one of the substances selected from the group consisting of a carboxylic acid, a soap, a metal soap, an alcohol, pentaerythritol, neopentyl glycol, a polyglycol a polyethylene glycol ether, an organic ester, a silane, a siloxane, a silicone oil, an organic sulfone of the formula RSO₂R, an organic ketone, an organic nitrile, an organic sulfoxide, an organic amide, a fatty acid ester and a fatty acid amide.
 27. The process according to claim 18, wherein the added amount of the second organic additive is from 0.01 to 10 wt. %, based on the finished coated product.
 28. The process according to claim 27, wherein the added amount of the second organic additive is from 0.015 wt. %, based on the finished coated product.
 29. The process according to claim 18, wherein the coated finely divided norganic solids have a mean particle size d₅₀ of from 0.005 to 5 μm.
 30. A composition comprising the inorganic solids produced by the process of claim 18 and a plastic.
 31. A composition comprising a paint and the inorganic solid produced by the process of claim
 18. 32. A composition comprising a ink and the inorganic solid produced by the process of claim
 18. 33. A composition comprising a paper and the inorganic solid produced by the process of claim
 18. 34. A composition comprising the inorganic solids produced by the process of claim 18 and a ceramic.
 35. A composition comprising the inorganic solids produced by the process of claim 18 and a medical adjuvant.
 36. A composition comprising the inorganic solids produced by the process of claim 18 and a cosmetic.
 37. A process comprising dispersing the coated finely divided inorganic solids produced by the process of claim 18 in water or an organic solvent to form a suspension, and adding an antifoam in an amount of up to 3 wt. %, based on the solids content of the suspension.
 38. A suspension comprising the particles coated solids prepared by the process of claim 18, or an organic solvent, and up to 3 wt. % of an antifoam based on the solids contact. 